ULTEM™ 9085 Overview
ULTEM™ 9085 is a high-performance polyetherimide intended for functional components requiring elevated-temperature capability, dimensional stability, and flame performance. The published values below are representative printed-specimen data and should be verified for the intended geometry and service environment.
Design Advantages
- Published tensile strength of 54 MPa for functional components
- Published tensile modulus of 2,050 MPa and flexural modulus of 2,170 MPa
- Glass transition temperature of 186 °C for elevated-temperature applications
- Base resin reported as UL 94 V-0 at 1.5 mm
Application Fit
- High-temperature fixtures, tooling, and functional prototypes
- Rigid structural brackets, housings, and load-bearing components
- Parts requiring a high-performance thermoplastic and documented flame rating
- Low-volume end-use components requiring application-specific qualification
Material Specifications
| Item | Published Value |
|---|---|
| Material family | Polyetherimide, ULTEM™ 9085 |
| Published density | 1.34 g/cm3 |
| Glass transition temperature | 186 °C |
| Heat deflection temperature | 158 °C at 0.45 MPa |
| Flammability rating | UL 94 V-0 at 1.5 mm, base resin |
| Published tensile strength | 54 MPa |
Material Properties
Physical and Mechanical Properties
| Property | Test Method | Published Value |
|---|---|---|
| Density | ISO 1183 | 1.34 g/cm3 |
| Tensile strength | ISO 527 | 54 MPa |
| Tensile modulus | ISO 527 | 2,050 MPa |
| Tensile elongation | ISO 527 | 3% |
| Flexural strength | ISO 178 | 90 MPa |
| Flexural modulus | ISO 178 | 2,170 MPa |
Thermal and Fire Properties
| Property | Test Method | Published Value |
|---|---|---|
| Glass transition temperature | DSC | 186 °C |
| Heat deflection at 0.45 MPa | ISO 75 | 158 °C |
| Flammability rating | UL 94 | V-0 at 1.5 mm, base resin |
Representative Printed-Specimen Conditions
| Parameter | Source Condition |
|---|---|
| Nozzle diameter | 0.4 mm |
| Layer height | 0.25 mm |
| Infill | 100% with ±45 degree raster |
| Extrusion temperature | 365 to 385 °C |
| Bed temperature | 130 to 140 °C |
| Specimen orientation | X/Y flat |
These conditions describe the source specimens and are not a universal processing specification. Equipment capability, geometry, thermal management, and material condition can require a different validated process window.
Design and Validation Considerations
- Treat the published values as representative data rather than guaranteed minimum properties.
- The published mechanical values are associated with X/Y-flat specimens; properties in other orientations were not reported in the source sheet.
- Validate anisotropy, layer bonding, dimensional stability, porosity, and surface condition using the intended production process.
- Verify sustained-temperature behavior, creep, fatigue, impact, wear, and chemical compatibility under the actual service conditions.
- The UL 94 V-0 result applies to the base resin at 1.5 mm; do not assume a printed finished part has the same classification without appropriate testing.
- For regulated or safety-critical applications, establish material traceability, process controls, inspection criteria, and part-specific qualification requirements.
Data Not Reported in the Source Sheet
| Design Input | Source Status |
|---|---|
| Directional Z properties | Not reported |
| Notched or unnotched impact strength | Not reported |
| Melting and crystallization temperatures | Not reported |
| Moisture absorption | Not reported |
| Chemical-resistance ratings | Not reported |
| Creep, fatigue, and wear data | Not reported |
Published Data and Qualification
The values in this sheet are based on published printed-specimen data documented by the material source and are provided for design reference and material comparison. Lucent Additive has not independently generated every published value. Final-part performance can differ because of geometry, orientation, material condition, processing, and service environment. This document does not create a material warranty or replace qualification of the customer’s finished component.